Preparation and Microanalysis Study of Nano-Hap/Cs-Chs Composites Materials

Abstract:

Article Preview

Nano-hydroxyapatite/chitosan-chondroitin sulfate composites materials with different weight ratios were prepared through liquid co-precipitation method. The nano-Hap、Hap/Cs and Hap/Cs-Chs composites materials under the same conditions preparation materials were researched By XRD, SEM and EDS respectively. The results show that nano-Hap particles with poorly crystallinity, the size is about 20nm, nano-Hap particles are spherical in sHape and dispersed uniformly, combined with relatively loose between particles, the small nano-particles aggregate into larger particles when the Hap composite with the Cs and Chs, nano-Hap were dispersed uniformly in the organic phase Cs and Chs, Hap particles have the trend to grow large in composites materials,crystal become more perfect, combination become relatively dense between particles, The composites materials were annealed at 700°C,Hap crystal particles become more perfect clear and larger with relatively loose between particles.EDS analysis showed that the compound before and after annealing of the material ratio of calcium had no influence, material does not contain any impurities,The ratio of calcium and phosphorus is about 1.75:1,Hap belonging to the type of calcium-rich

Info:

Periodical:

Advanced Materials Research (Volumes 581-582)

Edited by:

Jimmy (C.M.) Kao, Wen-Pei Sung and Ran Chen

Pages:

463-466

Citation:

M. D. Qiu et al., "Preparation and Microanalysis Study of Nano-Hap/Cs-Chs Composites Materials", Advanced Materials Research, Vols. 581-582, pp. 463-466, 2012

Online since:

October 2012

Export:

Price:

$38.00

[1] Patrícia C. Salgado, , et al. Journal of Biomaterials and Nanobiotechnology. (2011), 2, 318-328.

[2] Wang Yunqing , LU Tingli, et al. Materials Review(2011), 25(2): 125-130.

[3] Xin Lei; Su Jia-can. Journal of Traumatic Surgery(2011), 13(3): 272-275.

[4] Khaled R. Mohamed, et al. Materials Chemistry and Physics(2011), 130(1): 561-568.

[5] Fangfang Sun, Hongjian Zhou, et al. Acta Biomaterialia (2011), 7(11): 3813-3828.

[6] Wang Hao, ZHang Li-cheng, et al. Journal of Peking University (2011), 43(5): 730-735.

[7] Sun Zhen-zhen, Cai Ru-ru, et al. Journal of Xiamen University (2010), 49(5): 671-675.

[8] Murugan R, Panduranga Rao K. J Biomater Sci Polym Ed, (2003) 14: 457-468.

[9] Rangasamy Jayakumar, etal. Int. J. Mol. Sci. ( 2011), 12, 1876-1887.

[10] Jin Liming, Liu Wanshun, et al. Chinese Journal of Clinical Rehabilitation,. 2006, 10(1): 144-146.

[11] X.H. Zou, W.C. Foong, T. Cao, B.H. Journal of Dental Research(2004), 83: 880.

[12] Lv Cai-xia, YAO Zi-hua. Acta Materiae Compositae Sinica (2007) 24(1): 110-115.

[13] Feng Wang, Enyan Guo, et al Advances in Bioscience and Biotechnology,. (2010), 1, 185-189.