Research on Synthesis and Performance of Solvent-Free Aluminum-Plastic Composite Polyurethane Adhesive

Abstract:

Article Preview

A low-viscosity and solvent-free polyurethane adhesive was prepared with mixed polyester, polyether and IPDI as main raw materials. The influences of different moral ratios of polyester and polyether on reaction time, viscosity and water resistance, adhesive strength were researched. The effects of catalysts to adhesive were well discussed. The experimental results showed that polyurethane adhesives composed by mixed polyester and polyether had low viscosity and had better waterproof quality. The adhesives showed the best comprehensive properties when the mole ratio of OHs of polyether to OHs of polyester was 0.3/0.7. Catalysts added to this adhesive could speed the curing reaction, but it reduced the peel strength of the adhesives.

Info:

Periodical:

Edited by:

B. Xu and H.Y. Li

Pages:

9-13

Citation:

Q. Wang et al., "Research on Synthesis and Performance of Solvent-Free Aluminum-Plastic Composite Polyurethane Adhesive", Advanced Materials Research, Vol. 583, pp. 9-13, 2012

Online since:

October 2012

Export:

Price:

$38.00

[1] J. Zhang: China Printing and Packaging Study Vol. 3 (2011), p.9.

[2] Y.T. Luo, R.X. Luo, L.Y. Sun: Packaging Journal Vol. 3(2011), p.37.

[3] G. Malucelli, A Priola and F Ferrero: International Journal of Adhesion and Adhesives Vol. 25 (2005), p.87.

[4] M. Patri, S.K. Rath and U.G. Suryavansi: Journal of Applied Polymer Science Vol. 99(2006), p.884.

[5] Bianca B.R. Silva, Ruth M.C. Santana and Maria M.C.: Int J Adhes Adhes Vol. 30(2010), p.559.

[6] J.J. Guo, H.Y. Zhang: CHINA Plastics Industry Vol. 33(2005), p.53.

[7] F.X. Tian, M.L. Chen: Chemical Industry and Engineering Progress Vol. 21(2002), P. 179.

[8] P.L. Xu, S.Q. Zhang: Handbook of Polyurethane Materials (Chemical Industry Press, 2011).

[9] Z.X. Zhan: Polyurethane Industry Vol. 21(2006), p.28.

[10] H.J. Wang: The Research of Polyester polyurethane adhesive structure, morphology and adhesive properties (Beijing University of Chemical Technology, Beijing, 2011).