Preparation and Anti-Scratch Property of Supersonic-Particles-Deposited Coating on Magnesium Alloy


Article Preview

In order to protect magnesium alloy structure used in equipments, Al-based alloy coating on ZM5 magnesium alloy surface was prepared by Supersonic-Particles-Deposition(SPD). Microstructure,bonding strength,hardness, anti-scratch property of the deposited Al-based alloy coating were analyzed and tested using scanning electron microscope(SEM),energy dispersive spectrmomter(EDS), dualization stretching method and scratch testing machine. The results indicated that the coating was compacted with 1.19% porosity on superficial layer and 0.08% porosity on cross-section, respectively. The bonding strength value was 42.37MPa, moreover the interface was distinct and continuous,without defects such as ablation and impurity. Microhardness of the coating was about 1.3 times to that of uncoated substrate. The anti-scratch property of the processed coating improved obviously compared to Mg-substrate.



Edited by:

Huawu Liu, Yongxin Yang, Shijie Shen, Zhili Zhong, Laijiu Zheng and Peng Feng




X. M. Wang et al., "Preparation and Anti-Scratch Property of Supersonic-Particles-Deposited Coating on Magnesium Alloy", Advanced Materials Research, Vol. 627, pp. 756-760, 2013

Online since:

December 2012




[1] Binshi Xu. Remanufacture and Recycle Economy [M]. Beijing: Science Press, (2007). 08(in chinese).

[2] Zhenhua Chen. Magnesium[M]. Beijing: Chemical Industry Press, (2004). 07(in chinese).

[3] Weiping Li, Zhu liqun: Material Protection. Vol. 38 (2005), p.41(in chinese).

[4] Hélène Ardelean, Isabelle Frateur and Philippe Marcus: Corrosion Science. Vol. 50 (2008), p. (1907).

[5] Isler Duygu, Birol Yucel and Urgen Mustafa: International Journal of Material Forming, Vol. 3 (2010), p.747.

[6] Yu Kyong Kim, Man Hyung Lee, Madhav Nepane Prasad, IL Song Park, Min Ho Lee, Kyeong Won Seol and Tae Sung Bae: Advanced Materials Research, Vol. 47-50 (2008), p.1290.


[7] Rongchang Zeng, Chen Jun, Kuang Jun, Zhang Jin and Wang Ying: Rare Metals. Vol. 29 (2010), p.193.


[8] Li ping Wu, Jingjing Zhao, Yongping Xie and zhongdong Yang: Transactions of Nonferrous Metals Society of China. Vol. 20 (2010), p.630.

Fetching data from Crossref.
This may take some time to load.