An experimental study of RHEED intensity oscillations was performed on (111)B substrates which were misoriented by 1 or 2º towards [110], [2¯1¯1], or [¯211] orientations. The behavior of the RHEED oscillations on (111)B was similar to that on (001). However, the temperature at which the RHEED intensity oscillations began to appear on (111)B was lower than that on (001). The surface diffusion length of Ga on (111)B was evaluated by taking account of the supersaturation ratio of adatoms on the terrace.

T.Shitara, E.Kondo, T.Nishinaga: Journal of Crystal Growth, 1990, 99, 530-4