A mechanism was proposed for the production of pure edge strain-relieving interface dislocations in the SiGe/Si(001) system. Electron microscopic observations were made which were consistent with the mechanism.

C.R.Hall: Nondestructive Testing and Evaluation, 1996, 12[5], 315-21