The typical configurations which were caused by plastic deformation of grains in a polycrystal were analyzed. It was shown that the resultant inter-grain defects formed a 2-dimensional ensemble of Somigliana dislocations extended over the junction disclination skeleton.

A.A.Zisman, V.V.Rybin: Acta Materialia, 1996, 44[1], 403-7