It was shown that the conduction band mobility edge position, and especially the luminescence spectra, suggested that valence alternating pair defects had to exist in vitreous silica. The number density of such defects was expected to be of the order of 1019/cm3.

L.P.Ginzburg: Journal of Non-Crystalline Solids, 1994, 171[3], 164-71