Deformation twinning in the {332}<113> system of Ti-alloys in a pre-transition state was studied experimentally and theoretically. Mechanisms were proposed for β-phase lattice rearrangement into the twin orientation.

Twinning on the {332}<113> System in Unstable β-Titanium Alloys. V.S.Litvinov, G.M.Rusakov: Physics of Metals and Metallography, 2000, 90[S], 96-107