The conductivities of the melts were determined as a function of composition, for temperatures ranging from the melting point to 1100K (table 155). It was found that the equivalent conductivity, as a function of composition, could be described by the function:

σ (Scm2/mol) = 138.1880-27.1111x+46.0708x2-9.6058x3

H.P.Bossmann, J.Richter, N.Struck: Zeitschrift fur Naturforschung, 1991, 46a[1-2], 206-9

 

 

Table 155

Conductivity of Molten NaCl-xAgCl at 1100K

σ [S/cm] = a + bT + cT2

 

x

Tm

a

103b

106c

0.1

1045

2.4106

-0.1382

1.2033

0.3

975

-2.3050

8.9231

-3.0844

0.5

920

-3.0418

11.1563

-4.3720

0.7

840

-2.0197

10.0693

-4.0197

0.9

760

-1.0999

9.1442

-3.6281