The conductivities of the melts were determined as a function of composition, for temperatures ranging from the melting point to 1100K (table 174). It was found that the equivalent conductivity, as a function of composition, could be described by the function:

σ (Scm2/mol) = 95.2402-27.0949x-21.8486x2+101.5860x3

H.P.Bossmann, J.Richter, N.Struck: Zeitschrift fur Naturforschung, 1991, 46a[1-2], 206-9

 

 

Table 174

Conductivity of Molten RbCl-xAgCl at 1100K

σ [S/cm] = a + bT + cT2

 

x

Tm

a

103b

106c

0.1

950

-3.0069

6.7235

-2.1794

0.3

840

-2.8958

6.9217

-2.3967

0.5

640

-3.0314

8.0418

-3.1158

0.7

595

-2.6048

8.6010

-3.5244

0.9

680

-1.3782

8.5041

-3.4203