Ionic transport studies were made of fluorite phases which had rare-earth trifluoride contents of 20 to 40mol%. The crystals were prepared by using the Stockbarger technique, and impedance spectroscopy was used to measure the conductivity in a vacuum of about 0.01Pa. It was found that the results for each composition could be described by a Frenkel-type law. The conductivity of Ca0.64Ho0.36F2.36, at temperatures ranging from 389 to 758K, could be described by:

σT (SK/cm) = 2.4 x 104 exp[-0.604(eV)/kT]

The conductivity at 500K was equal to 4.0 x 10-5S/cm.

A.K.Ivanov-Shits, N.I.Sorokin, E.A.Krivandina, A.A.Samokhina, B.P.Sobolev: Elektrokhimiya, 1988, 24[11], 1571-4 (Soviet Electrochemistry, 1988, 24[11], 1458-61)