Migration in the amorphous alloy was studied, at between 575 and 643K, by using secondary ion mass spectrometry. The measurements were performed on pre-relaxed specimens, and it was found that the diffusion coefficients lay between 10-23 and 2 x 10-20m2/s. The results (table 153) could be described by:

D(m2/s) = 7.0 x 105 exp(-3.39(eV)/kT]

It was suggested that the diffusion mechanism involved the cooperative motion of groups of atoms.

S.K.Sharma, M.P.Macht, V.Naundorf: Acta Metallurgica et Materialia, 1992, 40[9], 2439-49