A decrease in the density of threading dislocations was observed during the epitaxial growth of GaN layers on porous SiC (PSC) substrates by means of chloride hydride vapour phase epitaxy. It was established that, in the early growth stage, the substrate was capable of redistributing stresses in the growing heterostructure, which leads to relaxation of the lattice misfit stresses via generation of a superlattice of planar defects. In the subsequent growth stage, these defects prevent the propagation of threading dislocations. Owing to this phenomenon, 1μm-thick GaN layers on PSC could be obtained with a

density of dislocations reduced by 2 orders of magnitude as compared to epilayers of the same thickness grown on nonporous substrates.