Rutherford back-scattering spectroscopy and nuclear reaction analysis were used to measure the diffusion coefficients of O (table 139) below 1000C.
E.Sonder, J.R.Martinelli, R.A.Zuhr, R.A.Weeks: Crystal Lattice Defects and Amorphous Materials, 1987, 15[1-4], 277-82
Table 139
Diffusion of O in MgO
Temperature (C) | D (cm2/s) |
845 | 2.90 x 10-20 |
895 | 1.70 x 10-19 |
974 | 2.40 x 10-19 |