The migration of H in the alloy (tables 24 and 25) was investigated by using the time-lag technique. Annealing the alloy at 400C led to the establishment of short-range order, and resulted in a decrease in the activation energies for H permeation and diffusion (tables 26 and 27).

V.B.Vykhodets, V.A.Goltsov, P.V.Geld: Fizika Metallov i Metallovedenie, 1968, 26[5], 933-5