The diffusion of H was investigated at 260 to 1000K by using electrochemical permeation and gas-phase permeation techniques. The temperature dependence of the diffusivity could be described by:

D (cm2/s) = 9.0 x 10-3 exp[-10.4(kcal/mol)/RT]

H.Hagi: Journal of the Japan Institute of Metals, 1983, 47[12], 1029-35

The best linear fits to the solute diffusion data ([678] to [681], [693] to [703], [717] to [722], [725] to [727], [730] to [733], [736] to [739], [756] to [758]) yield:

Ag: Ln[Do] = 0.38E – 18 (R2 = 0.86); Cu: Ln[Do] = 0.44E – 22 (R2 = 0.77);

In: Ln[Do] = 0.50E – 22.8 (R2 = 0.99); O(l): Ln[Do] = 0.26E – 8.4 (R2 = 0.79);

Zn: Ln[Do] = 0.29E – 14.4 (R2 = 0.87)