Self- and impurity-diffusion in Zr-Mn alloys (Mn-0.2at%) was studied by using the serial sectioning method at 1173 to 1473K. The results for 95Zr were described by:

D (cm2/s) = 3.1 x 10-5 exp[-25.1(kcal/mol)/RT]

The addition of Mn to Zr resulted in an enhancement of self-diffusion while retarding impurity diffusion. The results were consistent with a vacancy mechanism for diffusion.

D.D.Pruthi, M.S.Anand, R.P.Agarwala: Philosophical Magazine, 1979, 39[2], 173-82