The stacking-fault energies of alloys containing between 2.1 and 6.18at%As were deduced (table 1) from electron microscopic and selected-area diffraction observations.

Stacking Fault Energies of α-Cu-As Alloys. I.Yoshizawa: Physica Status Solidi A, 1973, 20[1], K7–9