Glide dislocations were studied by transmission electron microscopy, using the weak-beam technique. Dislocation glide planes, Burgers vectors and types (α or β) were identified. Both the α and β dislocations were found to be dissociated, with the dissociation widths corresponding to a stacking-fault energy of 85mJ/m2.