Samples in which x ranged from 0 to 0.9 were studied by using solid-state reaction. A black phase, Ag0.1-δMoO3, was found which had a monoclinic structure (a = 1.48326nm, b = 0.78826nm, c = 0.127533nm, b= 113.03°). The conductivity was determined by means of complex impedance spectrum analysis. The total conductivity of Ag0.1-δMoO3 was 9.89S/cm, whereas its electronic conductivity was 0.404S/cm. The electrical conductivity of other compositions varied in a regular manner as a function of composition.

S.Tian, F.Zhou, J.Yang, Z.Li: Solid State Ionics, 1992, 57[1-2], 109-12