Nuclear micro-analysis and cathodic hydrogenation were used to study D diffusion in the stainless steel. The D content was equal to about 20at%. The diffusivity at 298K was equal to 1.4 x 10-16m2/s.

M.B.Lewis, K.Farrell: Applied Physics Letters, 1980, 36[10], 819-21