Chemical Solution Deposition Growth of La0.7Ca0.3MnO3 Films and their Electric Pulse Induced Resistance Change Effect


Article Preview

A simple chemical solution deposition method was developed for the preparation of La0.7Ca0.3MnO3 (LCMO) thin films. The LCMO thin films were prepared on Si/SiO2/TiO2/Pt substrates by spin-coating method, followed by heat-treatment at 900°C. The fabrication process of the LCMO thin film was investigated by means of TG-DSC, FTIR, XRD, FE-SEM and EPMA. The electric pulse induced reversible resistance switching is observed in the Ag-LCMO-Pt sandwich structure.



Key Engineering Materials (Volumes 280-283)

Edited by:

Wei Pan, Jianghong Gong, Chang-Chun Ge and Jing-Feng Li




R. Dong et al., "Chemical Solution Deposition Growth of La0.7Ca0.3MnO3 Films and their Electric Pulse Induced Resistance Change Effect", Key Engineering Materials, Vols. 280-283, pp. 473-476, 2005

Online since:

February 2007




[1] R. von. Helmolt, J. Wecker, B. Holzapfel, L. Schultz and K. Samwer: Phys. Rev. Lett. Vol. 71 (1993), p.2331.


[2] S. Jin, T.H. Tiefel, M. McCormack, R.A. Fastnacht, R. Ramesh and L. H. Chen: Science, Vol. 264 (1994), p.413.

[3] A. Asamltsu, Y. Tomloka, H. Kuwahara and Y. Tokura: Nature Vol. 388 (1997), p.50.

[4] V. kiryukhin, D. Casa, J.P. Hill, B. Keimer, A. Vigliante, Y. Tomioka and Y. Tokura: Nature Vol. 386 (1997), p.813.


[5] S.Q. Liu, N.J. Wu and A. Lgnatiev: Appl. Phys. Lett. Vol. 76 (2000), p.2749.

[6] S.Q. Liu, N.J. Wu and A. Lgnatiev: US. Patent, 6204139B1, (2001).

[7] A. Baikalov, Y.Q. Wang, B. Shen, B. Lorenz, S. Tsui, Y.Y. Sun, Y.Y. Xue and C.W. Chu: Appl. Phys. Lett. Vol. 83 (2003), p.957.

[8] J. Fukushima, K. Kodaira and T. Matsushita: J. Mater. Sci. Vol. 19 (1984), p.595.

[9] L.H. Larry and K.W. Jon: Chem. Rev. Vol. 90 (1990), p.33.

[10] N.I. Kovtyukhova, E.V. Buzaneva, C.C. Waraksa, B.R. Martin and T.E. Mallouk: Chem. Mater. Vol. 12 (2000), p.383.

[11] A. Pohl, G. Westin and K. Jansson: Chem. Mater. Vol. 14 (2002), pp. (1981).

[12] S. Faaland, K.D. Knudsen, M.A. Einarsrud, L. Romark, R. Hojer and T. Grande: J. Solid State Chem. Vol. 140 (1998), p.320.

[13] C. Vazquez- Vazquez, M. Carmen Blanco, M. Arturo Lopez-quintela, R. D. Sanchez, J. Rivas and S. B. Oseroff: J. Mater. Chem. Vol. 8 (1998), p.991.


[14] S.Y. Bae and S.X. Wang: Appl. Phys. Lett. Vol. 69 (1996), p.121.