The precursor solution of titanium oxide coating was prepared by using titanium-oxygen sulfide. Solution with PH value of 8.5 was used to for coating on the surface of glass through dipping. The coatings were analyzed with DSC, AFM and XRD. The hydrophilic results of titanium oxide coating were obtained according the water contact angle measurement in the sunlight irradiation condition. The experimental results demonstrate that this solution is a good precursor for coating of titanium oxide, and the coatings treated at a higher temperature have shown good hydrophilic property.