Influence of Solvent Polarity on Synthesis of Beta - Tricalcium Phosphate

Abstract:

Article Preview

Beta tricalcium phosphate (β - TCP) has been synthesized at relatively low temperature. The reaction product has been characterized by XRD, FT-IR and TEM. It is found that the polarity of synthesis media plays an important role in the formation of β - TCP crystal phase. In light of XRD, FT-IR and TEM results, the difference of reaction product between high and low polarity synthesis media might be attributed to carbonate groups, which might suppress the phase transformation process.

Info:

Periodical:

Key Engineering Materials (Volumes 330-332)

Main Theme:

Edited by:

Xingdong Zhang, Xudong Li, Hongsong Fan, Xuanyong Liu

Pages:

143-146

Citation:

X. L. Deng et al., "Influence of Solvent Polarity on Synthesis of Beta - Tricalcium Phosphate", Key Engineering Materials, Vols. 330-332, pp. 143-146, 2007

Online since:

February 2007

Export:

Price:

$38.00

[1] K. Itatani, T. Nishioka, S. Seike, et al.: J Am Ceram Soc Vol 77(3) (1994), p.801.

[2] A. C. Tas, F. Korkusus, M. Timucin, et al.: J Mater Sci Mater Med Vol 8 (1997), p.91.

[3] M. Akao, H. Aoki, K. Kato, et al.: J Mater Sci Vol 17 (1982), p.343.

[4] P. Layrolle, A. Lebugle.: Chem Mater Vol 6(1994), p. (1996).

[5] S. C. Liou, S. Y. Chen: Biomaterials Vol 2(2002)3, p.4541.

[6] R. Famery, N. Richard, P. Boch: Ceram Int Vol 2(1994), p.327.

[7] Bigi, E. Foresti, M. Gandolfi, et al: J Inorg Biochem Vol 66 (1997), p.259.

[8] Y. Pan, J. L Huang, C. Y Shao: J Mater Sci Vol 38(2003), p.1049.

[9] Y. Yokogawa, Y. Kawamoto, M. Toriyama, et al.: J Ceram Soc Jpn Vol 99 (1991), p.28 Figure 3 TEM images of samples prepared with (a) H2O (50) +C2H5OH (50) and (b) C2H5OH.

[10] R. Z. LeGeros: Clin Orthop Vol 395 (2002), p.81.

[11] M. Vallet-Regi, L. M. Rodriguez-Lorenzo, A. J. Salinas: Solid State Ionic 101-103(1997), p.1279.

[12] E. V. Kalinkina, A. M. Kalinkin, W. Forsling, et al: Int J Miner Process 61(2001), p.273.

[13] J. L. Arias, F. J. Garcia-Sanz, M. B. Mayor, et al.: Biomaterials 19(1998), p.883.

[14] E. I. Suvorova, F. Christensson, H. E. L. Madsen, et al. J Cryst Growth 1: 86(1998), p.262.

[15] C. Mao, H. Li, F. Cui, et al.: J Cryst Growth 206(1999), p.308.

Fetching data from Crossref.
This may take some time to load.