Effect of Al(Cr) Content on the Distribution of Al2O3(Cr2O3) Particles Formed by Internal Oxidation


Article Preview

This investigation was conducted to study the effect of Al(Cr) content in Cu-Al(Cr) pre-alloyed powders on the distribution of Al2O3(Cr2O3) particles formed by internal oxidation. The results show that the distribution of Al2O3 particles is different with the change of Al content in Cu-Al system. When the Al content is above 1.2wt.%, the Al2O3 particles tend to distribute along the grain boundaries of copper matrix , whereas when the Al content is above 2.0 wt.%, the Al2O3 particles have distributed along the grain boundaries. However, it is interesting to note in Cu-Cr system that most of the formed Cr2O3 particles prefer to distribute in the grain of copper matrix when the Cr content is less than 5wt.%, which is quite different from that of Cu-Al system.



Key Engineering Materials (Volumes 334-335)

Edited by:

J.K. Kim, D.Z. Wo, L.M. Zhou, H.T. Huang, K.T. Lau and M. Wang




S. H. Liang et al., "Effect of Al(Cr) Content on the Distribution of Al2O3(Cr2O3) Particles Formed by Internal Oxidation ", Key Engineering Materials, Vols. 334-335, pp. 189-192, 2007

Online since:

March 2007




[1] Joanna Groza. Heat-Resistant. Journal of Materials Engineering and Performance. 1 (1) (1992) , pp.113-121.

[2] J. F. Perez and D. G. Morris. Scripta Metallurgica. 31: (3)(1994), pp.231-235.

[3] Lee D. W., Kim B. K. Materials Letters. 58(3-4)(2004), pp.378-383.

[4] Samal P. K. Metal Powder Report. 39 (10) (1984), pp.587-589.

[5] F. H. Stott, G. C. Wood. Materials Science and Technology A. 4 (12) (1988) , pp.1072-1078.

[6] D. Y. Ying, D. L. Zhang. Materials Science and Engineering A, 286(2000), pp.152-156.

[7] Liang Yingjiao. Physical Chemistry. Metallurgy Industry Publishing Company, Beijing, 1983, pp.236-263.

[8] Shuhua Liang. In-situ prepared Cu/Al2O3(Cr2O3) composites and their preparation mechanism[D]. Xian jiaotong university, (2004).

Fetching data from Crossref.
This may take some time to load.