Fabrication and Properties of SrBi2(Ta1-xNbx)2O9 Ferroelectric Ceramics

Abstract:

Article Preview

SrBi2(Ta1-xNbx)2O9(SBTN) ferroelectric ceramics with typical bismuth layered perovskite structure were synthesized with a reactive hot-press sintering process at 1000°C for 2h. The as-sintered SBTN (x=0.2, 0.4, 0.6, 0.8) materials had a maximum relative density of 95.97%. Bi-layered perovskite structure was obtained. The grain sizes increased with increasing Nb content. In 1MHz frequency, remanent polarization (Pr) of SBTN (x=0.2, 0.4, 0.6, 0.8) were 10.0, 3.0, 1.7 and 1.0, while coercive field (Ec) of SBTN (x=0.2, 0.4, 0.6, 0.8) were 50, 32, 33 and 33kV/cm, respectively.

Info:

Periodical:

Key Engineering Materials (Volumes 336-338)

Edited by:

Wei Pan and Jianghong Gong

Pages:

143-145

DOI:

10.4028/www.scientific.net/KEM.336-338.143

Citation:

W. Wang et al., "Fabrication and Properties of SrBi2(Ta1-xNbx)2O9 Ferroelectric Ceramics", Key Engineering Materials, Vols. 336-338, pp. 143-145, 2007

Online since:

April 2007

Export:

Price:

$35.00

[1] D. H. Bao, Z. H. Wang, W. Ren, L. Y. Zhang and X. Yao: Ceram. Inter. Vol. 25 (1999), p.261.

[2] C. A. Araujo, J. D. Cuchiare, L. D. Mcminan, M. C. Scott and J. F. Scott: Nature Vol. 374 (1995), p.627.

[3] N. S. Prasad, K. B. Varma: Mater. Sci. Eng. B Vol. 90 (2002): 246.

[4] X. M. Chen, G. L. Hu, J. S. Yang: J. Europ. Ceram. Soc. Vol. 20 (2000), p.1257.

In order to see related information, you need to Login.