Microwave Dielectric Properties of (1-x)(Ca0.61Nd0.26)TiO3–x(Li0.5Sm0.5)TiO3


Article Preview

(1-x)(Ca0.61Nd0.26)TiO3-x(Li0.5Sm0.5)TiO3 (0.2 ≤ x ≤ 0.7) ceramics were prepared by solid-state reaction method and the microwave dielectric properties of the resultant materials at different (Li0.5Sm0.5)TiO3 contents were investigated. A single phase of perovskite in all samples was confirmed by XRD patterns. With increasing (Li0.5Sm0.5)TiO3 content, Q×f value and dielectric constant (εr) decrease slightly and the temperature coefficients of the resonant frequency (τf) of the specimens decreases noticeably. The optimum parameters, i.e.,εr = 109, Q×f = 5259 GHz and τf = ~0 ppm/°C, for the composition of 0.4(Ca0.61Nd0.26)TiO3-0.6(Li0.5Sm0.5)TiO3 was obtained when keep the calcination temperature at 1250°C for 3 h.



Key Engineering Materials (Volumes 336-338)

Edited by:

Wei Pan and Jianghong Gong




W. Wang et al., "Microwave Dielectric Properties of (1-x)(Ca0.61Nd0.26)TiO3–x(Li0.5Sm0.5)TiO3", Key Engineering Materials, Vols. 336-338, pp. 287-289, 2007

Online since:

April 2007




[1] W. Wersing: Mater. Sci. Forum Vol. 1 (1996), p.715.

[2] E.S. Kim, B.S. Chun and K.S. Bang: Ceram. Soc. Vol. 38 (2001), p.672.

[3] M. Yoshida, N. Hara and T. Takada: Jpn. J. Appl. Phys. Vol. 36 (1997), p.6818.

[4] W.E. Courtney: Microwave Theor. Tech. Vol. 18 (1970), p.476.

[5] W.S. Kim, K.H. Yoon and E.S. Kim: Jpn. J. Appl. Phys. Vol. 39 (2000), p.5650.

Fetching data from Crossref.
This may take some time to load.