Dielectric Properties of Y3+-Doped Ba0.62Sr0.38TiO3 Ceramics


Article Preview

Microstructure and dielectric properties of Ba0.62Sr0.38TiO3 ceramics doped with x mol% (x=0.2~0.6) Y2O3 were investigated. SEM showed that Y3+ can accelerate growth of the grains at first, then turn to inhabit growth of the grains with further addition of Y3+ above 0.8mol%. The experimental results showed that the dielectric constants were improved with the additive amount of Y3+ increasing, if the amount of Y3+ increased continuously, the dielectric constants will drop, whereas the dielectric losses of the samples descended rapidly in the beginning, then went up obviously with further addition of Y3+ above 1.0mol%, the optimal dielectric constant and dielectric loss could reach 6700 and 0.0015 in the room temperature, respectively.



Key Engineering Materials (Volumes 336-338)

Edited by:

Wei Pan and Jianghong Gong




Y. L. Li et al., "Dielectric Properties of Y3+-Doped Ba0.62Sr0.38TiO3 Ceramics", Key Engineering Materials, Vols. 336-338, pp. 51-53, 2007

Online since:

April 2007




[1] B. Wu, L. Zhang and X. Yao: Ceram. Int. Vol. 30(2004), p.1757.

[2] Y. Tsau, Y. Chen, H. Cheng and I. Lin: J. Eur. Ceram. Soc. Vol. 21(2001), p.1561.

[3] Y. Qu, D. Shan, J. Song, et al.: Rare Metal Mater. Eng. Vol. 34 [suppl. 1] (2005), p.774.

[4] D. Shan, Y. Qu, C. Zhang, et al.: Rare Metal Mater. Eng. Vol. 34 [suppl. 1] (2005) p.777.

[5] M.T. Buscaglia, M. Viviani, V. Buscaglia, et al.: J. Am. Ceram. Soc. Vol. 85(2002), p.1569. Fig. 3 Temperature dependence of dielectric constants of samples sintered 1300°C for 2h.