Application of Wear Resistant Coating Technology on Coating Blade

Abstract:

Article Preview

Coating blade wears seriously in paper coating process. Wear mechanism was analyzed in this article. A new technology of surface coating process was introduced to increase the hardness of the edge of coating blade and thus to prolong its service life. Surface coating preparing process on blade was studied and metal-ceramic compound coating prepared successfully on the edge of coating blade with AT13 (Al2O3+13%TiO2) wear resistant material by plasma spraying process. NiCrAl alloy powder was used as under coat material. Microstructure of the coating is dense. The coating bonds well with the matrix and have high hardness. Results of grain-abrasion testing show that wear-resisting property of the metal/ceramic compound coating is about 7-8 times as that of steel blade.

Info:

Periodical:

Key Engineering Materials (Volumes 353-358)

Edited by:

Yu Zhou, Shan-Tung Tu and Xishan Xie

Pages:

1761-1764

Citation:

C. M. Wang et al., "Application of Wear Resistant Coating Technology on Coating Blade", Key Engineering Materials, Vols. 353-358, pp. 1761-1764, 2007

Online since:

September 2007

Export:

Price:

$38.00

[1] YANG Zaohao: World Pulp and Paper Vol. 20 (2001), p.6.

[2] GUO Yalong: China Pulp & Paper Industry Vol. 26 (2005), p.44.

[3] B. K. Kim, D. W. Lee and C. J. Choi: Powder Metallurgy Vol. 44(2001), p.275.

[4] XU Wenji, GAO Yuan, Zhou Jinjin and MA Tengca: Material Protection Vol. 35(2002), p.46.

[5] Serdar Salman, Ramazan Köse , Levent Urtekin and Fehim Findik: Materials and Design Vol. 27 (2006), p.585.

DOI: https://doi.org/10.1016/j.matdes.2004.12.010

[6] S. C. Tjong, K. C. Lau, J. S. Ku and N. J. Ho: Surface Engineering Vol. 15(1999), p.490 Fig. 4 Surface of samples after grain-abrasion (a) T10A (b) AT13 coating (a) (b).

Fetching data from Crossref.
This may take some time to load.