Experimental Study on Residual Stress of K24 Superalloy in Laser Cladding Zone by Laser Shock Processing

Abstract:

Article Preview

The surface of K24 superalloy was processed with laser cladding & LSP (laser shock processing). Residual stress in the laser cladding zone by LSP was measured with X-ray stress tester X-350A, and the variational rule of residual stress in the cladding zone by tempering treatment of 8 hours and 16 hours was measured, respectively. The experimental results show that compressive residual stress of K24 superalloy surface by laser cladding & laser shock processing is above -600MPa, which exceeds residual stress by mechanical peening treatment; and there is no clear effect on residual stress by tempering treatment at 600°C for 8 hours and 16 hours, respectively, which can improve fatigue life of K24 superalloy.

Info:

Periodical:

Key Engineering Materials (Volumes 353-358)

Edited by:

Yu Zhou, Shan-Tung Tu and Xishan Xie

Pages:

453-456

Citation:

J. Z. Lu et al., "Experimental Study on Residual Stress of K24 Superalloy in Laser Cladding Zone by Laser Shock Processing", Key Engineering Materials, Vols. 353-358, pp. 453-456, 2007

Online since:

September 2007

Export:

Price:

$38.00

[1] Thord Thorslund, Franz-Josef Kahlen, Aravinda Kar: Optics and Lasers in Engineering, Vol. 39 (2003), pp.51-71.

DOI: https://doi.org/10.1016/s0143-8166(02)00040-4

[2] Y. K. Zhang, C.L. Hu, L. Cai: Appl. Phys. A, Vol. 72 (2) (2001), pp.113-116.

[3] J. C. Yang, J.Z. Zhou, Y.K. Zhang: Journal of Jiangsu University, Vol. 23(1) (2002), pp.1-4.

[4] Y. K. Zhang: Fatigue life improvement of the aero Al-Alloy by laser shocking, NanJing university of aeronautics and astronautics, 1995, pp.25-26.

[5] K. H. Richter, S. Orban, S. Nowotny: Proceedings of the 23rd International Congress on Applications of Lasers and Electro-Optics, (2004).

[6] W. J. Huo, H. G Sun: Aviation service, Vol. 11(6) (2001), pp.12-14.

[7] W. Y. Guo, D.S. Wang, M.C. Wang: Applied Laser, Vol. 22(2) (2003), pp.101-104.

[8] A. X. Feng Y.K. Zhang: Key Engineering Materials, Vols. 315-316(2005), pp.264-268.

Fetching data from Crossref.
This may take some time to load.