Research on Hot Upsetting Deformation Behavior and Dynamic Recrystallization for AZ31

Abstract:

Article Preview

The AZ31 Mg alloy was upseted from 250°C to 500°C. In optical microscopy, as the temperature increases, the volume fraction of deformation twin will reduce to a minium and vanish. Simultaneously, some small dynamically recrystallized grains were observed at the boundaries of origin grains and twins. When temperatures rise from 350°C to 500°C , the volume fraction and size of DRX grains increases .By the compression test of the upsetting proof samples, the compressive strength reach a maxium, and reduce during further rising temperatures.

Info:

Periodical:

Key Engineering Materials (Volumes 353-358)

Edited by:

Yu Zhou, Shan-Tung Tu and Xishan Xie

Pages:

722-725

DOI:

10.4028/www.scientific.net/KEM.353-358.722

Citation:

W. H. Hu et al., "Research on Hot Upsetting Deformation Behavior and Dynamic Recrystallization for AZ31", Key Engineering Materials, Vols. 353-358, pp. 722-725, 2007

Online since:

September 2007

Export:

Price:

$35.00

[1] S. Lee,Y. H. Chen, J. Y. Wang: J. Mater. Process Technol. Vol. 124 (2002), p.19.

[2] H. Takuda, T. Enami, K. Kubota: J. Mater. Proc. Technol. Vol. 101 (2000), p.281.

[3] H. Takuda, H. Fujimoto, N. Hatta: J. Mater. Process Technol. Vol. 80-81(1998), p.513.

[4] J. Becker, G. Fischer, K. Schemme, O. Fuchs, in: B. L. Mordike, K. U. Kainer (Eds. ), Proceedings of the International Conference on Magnesium Alloys and their Applications, Frankfurt, Werk stoff Informations gesells chaft (1998), p.15.

[5] P. Klimanek, A. potzsch: Mater. Sci. Eng. A Vol. 324 (2002), p.145.

[6] R. Kaibyshev, A. Galiev and O. Sitdikov: Nanostruct. Mater. Vol. 5-8 (1995), p.621.

[7] Sitikov O, Kaibyshev R, Sakai T: Mater. Sci. Forum Vol. 419-422 (2003), p.521.

[8] Yin D LWang K. FHan W B: Mater. Sci. Eng. A Vol. 392 (2005), p.320.

In order to see related information, you need to Login.