Preparation and Phase Analysis of Fe-SiAlON-MoSi2 Composites

Abstract:

Article Preview

Fe-SiAlON-MoSi2 composites were prepared using FeSi75, α-Al2O3, and MoSi2 powders as starting materials at 1400 oC, 1500 oC, 1600 oC and 1700 oC, respectively, for 3h in a flowing nitrogen under the pressure of 0.9MPa. The results showed that the main phases of Fe-SiAlON-MoSi2 composite were β-SiAlON with deferent Z-values, MoSi2, and Fe3Si. Z-value of the obtained β-SiAlON depanded on α-Al2O3 content and the sintering temperature. The morphology of SiAlON phase changed from fibre-like of low Z-value to hexagonal prism-like of high Z-value.

Info:

Periodical:

Key Engineering Materials (Volumes 368-372)

Edited by:

Wei Pan and Jianghong Gong

Pages:

1123-1125

DOI:

10.4028/www.scientific.net/KEM.368-372.1123

Citation:

J. Z. Yang et al., "Preparation and Phase Analysis of Fe-SiAlON-MoSi2 Composites", Key Engineering Materials, Vols. 368-372, pp. 1123-1125, 2008

Online since:

February 2008

Export:

Price:

$35.00

[1] O. Sbaizero , S. Roitti , G. Pezzotti.: Mater. Sci. & Eng. Vol. 359 A (2003), p.297.

[2] N.L. Savchenko, P.V. Korolev, A.G. Melnikov, et al.: Wear. Vol. 249 (2002), p.892.

[3] D.Z. Wang, T. Y. Zuo, X. Y. Liu: Materials Review (Chinese) Vol. 11 (1997), p.53.

[4] J.X. Shen, Y. H. Ma: Advanced Ceramics (Chinese).

[1] (2000), p.15.

[5] J.H. Chen, J. L. Sun, W. D. Xue, et al.: Iron Alloy (Chinese).

[3] (2004), p.17.

[6] J.H. Han, M. X. Jiang, L. Wang, et al.: Refractories (Chinese) Vol. 4.

[3] (2006), p.181.

[7] J.Z. Yang, Z.H. Huang, Y.F. Xia, et al.: Rare Metal Mater. Eng. Vol. 36[Suppl. 2] (2007), P. 273.

[8] W.M. Sui, Y. Huang: Bulletin of the Chinese Ceramic Society.

[1] (2000), p.47.

[9] Z.H. Huang, J.L. Sun, J. X. Wang: Refractories (Chinese) Vol. 35.

[3] 2001), p.125.

In order to see related information, you need to Login.