Fabrication and Conductivities of CeO2-Based Oxygen-Ion Conductors Doped by M2O3 (M=La, Nd, Sm and/or Ga)


Article Preview

Ceria oxygen-ion conductors doped with M2O3 (M=La, Nd, Sm and/or Ga) were prepared by a wet chemical method. Phases were analyzed by X-ray diffraction method and conductivities were measured by using AC impedance analyzer. The results showed that Ga2O3-CeO2 solid solution with 17 nm grains and pure fluorite phase had been obtained even at calcination temperature of 800 °C for 5 hs. Conductivities of Ga2O3-La2O3 co-doped CeO2 were higher than that of Sm2O3-doped CeO2, which was reported having the highest conductivity among CeO2-based oxides.



Key Engineering Materials (Volumes 368-372)

Edited by:

Wei Pan and Jianghong Gong




H. Zhang et al., "Fabrication and Conductivities of CeO2-Based Oxygen-Ion Conductors Doped by M2O3 (M=La, Nd, Sm and/or Ga)", Key Engineering Materials, Vols. 368-372, pp. 244-246, 2008

Online since:

February 2008




[1] N. Miura, H. Kurosawa, M. Hasei, et al.: Soilid State Ionics Vol. 86-88 (1996), p.1069.

[2] W. Huang, P. Shuk, M. Greenblatt, et al.: J. Electrochem. Soc. Vol. 147 (2000), p.4196.

[3] R.A. George and N.F. Bessette: J. Power Sources Vol. 71 (1998), p.131.

[4] T. Kudo and H. Obayashi: J. Electrochem. Soc. Vol. 123 (1976), p.415.

[5] P.D. Batle, C.R.A. Catlow, J.W. Heap et al.: J. Solid State Chem., Vol. 63 (1986), p.8.

[6] T. Ishihara, T. Shibayama, S. Ishikawa, et al.: J. Europ. Ceram. Soc. Vol. 24 (2004), p.1329.

[7] H. Inaba and H. Tagawa: Solid State Ionics Vol. 83 (1996), p.1.

[8] T. Mori, T. Ikegami and H. Yamamura: J. Electrochem. Soc. Vol. 146 (1999), p.4380.

[9] F.Y. Wang, S. Chen and S. Cheng: Electrochem. Commun. Vol. 6 (2004), p.743.

[10] Z.C. Li, H. Zhang, B. Bergman, et al.: J. Europ. Ceram. Soc. Vol. 26 (2006), p.2357.

[11] M. Mogensen, D. Lybye, N. Bonanos, et al.: Solid State Ionics Vol. 174 (2004), p.279.

Fetching data from Crossref.
This may take some time to load.