Preparation of Aluminum Oxynitride Powder by Solid State Reaction Method

Abstract:

Article Preview

Single-phase aluminum oxynitride powders were obtained by varying the holding temperature (T) and the weight percentage of α-Al2O3 in Al2O3 (X) with nano-sized Al2O3 and AlN powders as raw materials. Influences of T and X on the phase composition of obtained powders were studied. The results showed that the content of aluminum oxynitride increased with increasing T or X. When X was 50% and T was 1750°C, obtained powders had better properties than those of others.

Info:

Periodical:

Key Engineering Materials (Volumes 368-372)

Edited by:

Wei Pan and Jianghong Gong

Pages:

435-437

Citation:

J. S. Wen et al., "Preparation of Aluminum Oxynitride Powder by Solid State Reaction Method", Key Engineering Materials, Vols. 368-372, pp. 435-437, 2008

Online since:

February 2008

Export:

Price:

$38.00

[1] X. D. Wang, W. C. Li and S. Seetharaman: Scand. J. Metal. Vol. 31 (2002), p.1.

[2] S. Bandyopadhyay, G. Rixecker, F. Aldinger, et al.: J. Am. Ceram. Soc. Vol. 85 (2002), p.1010.

[3] H.X. Willems: PhD Thesis (Technical University of Eindhoven, Eindhoven, Holland, 1992).

[4] Information on http: /www. arl. army. mil/wmrd/Tech/TransparentArmor-both. pdf.

[5] W. F. Miao: USA Patent 20050118086 (2005).

[6] J. W. McCauley: J. Am. Ceram. Soc. Vol. 61 (1978), p.372.

[7] J. W. McCauley and N. D. Corbin: J. Am. Ceram. Soc. Vol. 62(1979), p.459.

[8] T. M. Hartnett, E. A. Maguire, R. L. Gentilman, et al.: Ceram. Eng. Sci. Proc. Vol. 3(1982), p.67.

[9] G. D. Quinn, N. D. Corbin, and J. W. McCauley: Am. Ceram. Soc. Bull., Vol. 63(1984), p.723.