Structure and Properties Investigation about a Copper-Base SHS Welding Material


Article Preview

A new Copper-base SHS welding material was developed to meet the demand of the welding mend about metal parts in field. The structure and properties of the welding line were studied and the results indicated that the welding was belong to fusion welding, the fusion area between the parent metal and the welding line was clear, the tensile strength of the welding line over 200MPa, the bend strength close to 600MPa and the surface hardness close to HRB130. All these indicated that this copper-base material could be used in emergency maintenance welding about metal parts.



Key Engineering Materials (Volumes 373-374)

Main Theme:

Edited by:

M.K. Lei, X.P. Zhu, K.W. Xu and B.S. Xu




J.Z. Hu et al., "Structure and Properties Investigation about a Copper-Base SHS Welding Material", Key Engineering Materials, Vols. 373-374, pp. 505-508, 2008

Online since:

March 2008




[1] Merzhanov A G. Self2propagating High-temperature Synthesis: Twenty Years of Search and Findings[M]. In: Combustion and Plasma Synthesis of High-temperature Materials, Ed by Munir Z A. VCH. New York: (1990).

[2] Li S J. Jioning of SiC Ceramics to Ni-Based Superalloy with Cu Intermediate Layer[J]. Key Engineering Materials, 2002, Vol27: 101~110.

[3] Qiang Li, Jing-yuan Yu, Bo-chun Mo. A Brief Introduction to Self-propagation in High Temperature Synthesis (SHS) Technique. Journal of Liaoning Institute of Technology [J], 2001 (10): 61-63(in Chinese).

[4] Zhi-yuan Wang. Progress of Research and Application on Self-propagating High-temperature Synthesis Technology. Chemical Industry and Engineering Progress [J], 2002 (3): 175-178(in Chinese).

[5] Sheng Yin. Combustion Synthesis [M]. Beijing: Metallurgical Industry Press, 1999. (in Chinese).