Study on Anti-Corrosion Epoxy Resin Coating without Solvent

Abstract:

Article Preview

The new paint of environment-friendly was fabricated that TDE-85 and other materials incorporation into epoxy resin enhanced tenacity, strength, thermal stability, humidity resistance and corrosion resistance due to its inherent flexibility. The paint’s viscosity is less 1000mPa·s in 25°C, can spread directly. Result of the corrosion velocity test indicates the coating’s corrosion velocity in 3.5% salt-liquor less than 0.02 g/m2h. The bending and shearing strength of EW-200 buildup epoxy resin is 649MPa and 57MPa in 25°C. The strength is stable after placing -30°Cfor 12h and 65°C for 12h. The scanning electro photomicrograph shows the type of failure breaking is a tough fracture.

Info:

Periodical:

Key Engineering Materials (Volumes 373-374)

Main Theme:

Edited by:

M.K. Lei, X.P. Zhu, K.W. Xu and B.S. Xu

Pages:

531-534

DOI:

10.4028/www.scientific.net/KEM.373-374.531

Citation:

Q. Huang et al., "Study on Anti-Corrosion Epoxy Resin Coating without Solvent", Key Engineering Materials, Vols. 373-374, pp. 531-534, 2008

Online since:

March 2008

Export:

Price:

$38.00

[1] LI Jin-gui, China Surface Engineering, 2004, 17(5): 5~10.

[2] XU Bin-shi, Ma Shi-Ning, et al, Paint &Coatings Industry, 2004, 34(9).

[3] Hoisington M.A. et al, Poly. Mat. Sci. And Eng., 1996, 74, 240~241.

[4] WU Shi-zhen, et al, Journal of TIANJIN Polytechnic UNIVERSIT, 2005, 24(6): 30~33.

[5] Hoisington M.A. et al, Poly. Mat. Sci. And Eng., 1996, 74, 240~241.

[6] WU Hang, China Materials Engineering Canon, (16) Paint Finishing, Chemistry Industry Press, (2006).

[7] CHEN Ping, LIU Li Zhu, et al, Acta Polymerica Sinica, 1994, (6): 641~645.

[8] GAO J W, Modern Test-Technology of Polymer, Beijing University of Aviation and Aircraft Press, 1999. (a)bending sample (b)shearing sample Fig. 5 SEM photographs of the fractured surface of bending and shearing sample.

In order to see related information, you need to Login.