Synthesis and Characterization of Spinel-Type NiCr2O4 Nanocrystalline

Abstract:

Article Preview

In this article, spinel–type NiCr2O4 Nanocrystalline were prepared by the citrate method. After doping it into P25 (degussa, TiO2), NiCr2O4/TiO2 thin film photoanode were prepared by screen printing process on the surface of Fluorine Tin Oxide (FTO) Glass. And then they were assembled into Dye sensitized TiO2 Nanocrystalline solar cells (DSSC). The as–prepared NiCr2O4 powders were characterized by differential thermal analysis/thermo gravimetry (DTA/TG), X–ray diffraction (XRD) and ultraviolet visible (Uv–Vis) diffuse spectra. The properties of the solar cells were investigated by Solar Simular and Keithley Sourcemeter, respectively. The results showed that the grain size of the NiCr2O4 particles obtained at optimum synthesis temperature (1000 °C) was about 40.23 nm and the band gap was 1.8ev. The cell properties increased when the doping amount of NiCr2O4 was 1wt%. The open–circuit voltage (Voc) of Dye Sensitized TiO2 Nanocrystalline Solar Cell was from 0.71V up to 0.73V, The short–circuit photocurrent (Jsc) of DSSC increased from 5.21mA·cm-2 to 6.95mA·cm-2. The photoelectric conversion efficiency (η) was from 2.40% up to 3.14%, which was 30.8% higher than the pure TiO2 thin film photoanode.

Info:

Periodical:

Key Engineering Materials (Volumes 512-515)

Edited by:

Wei Pan and Jianghong Gong

Pages:

86-90

DOI:

10.4028/www.scientific.net/KEM.512-515.86

Citation:

Z. Q. Hu et al., "Synthesis and Characterization of Spinel-Type NiCr2O4 Nanocrystalline", Key Engineering Materials, Vols. 512-515, pp. 86-90, 2012

Online since:

June 2012

Export:

Price:

$38.00

[1] L. Fan, W. J. Huai and L.J. Ming, Synthesis, characterization and photocatalytic properties of nanocrystalline CuAl2O4, J. Sciencepaper Online. 3(2008) 263-267.

[2] J.Y. Yan, L.J. Gang and N.G. Ling, Preparation and visible light photocatalytic property of spinel CuAl2O4 nanoparticles, J. Journal of the Chinese Ceramics Society. 34(2006) 1084-1807.

[3] S.K. Patdeshi and R.Y. Pawar, Optimization of reaction conditions in selective oxidation of styrene over fine crystallite spinel-type CaFe2O4 complex oxide catalyst, J. Materials Research Bulletin. 45(2010) 609-615.

DOI: 10.1016/j.materresbull.2010.01.011

[4] M.S. Niasari, A. Davar and M. Farhadi, Synthesis and characterization of spinel-type CuAl2O4 nanocrystalline by modified sol–gel method, J. Chemistry and Materials Science. 51(2009)48-52.

DOI: 10.1007/s10971-009-1940-3

[5] O. Crottaz, F. Kubelb, H. Schmida, Jumping crystals of the spinels NiCr2O4 and CuCr2O4, J. Mater Chem. 7(1997) 143-146.

DOI: 10.1039/a604758k

[6] J. Słoczyński, B. Grzybowska, R. Grabowski, Oxygen adsorption and catalytic performance in oxidative dehydrogenation of isobutane on chromium oxide-based catalysts, J. PCCP. 1(1999)333-339.

DOI: 10.1039/a806136j

[7] Y. Lee, J. Chae, M. Kang, Comparison of the photovoltaic efficiency on DSSC for nanometer sized TiO2 using a conventional sol-gel and solvothermal methods, J. Journal of Industrial and Engineering Chemistry. 403(2010)609-614.

DOI: 10.1016/j.jiec.2010.03.008

[8] N.S. Pesika, K.J. Stebe, P.C. Searson, Determination of the particle Size Distrbution of Quantum Nanoctytals from Absorbance Spectra, J. Adv Mater. 15(2003) 1289-1291.

DOI: 10.1002/adma.200304904

[9] J. Z. Guo, Semiconductor Physics, Zhe jiang University Press, Hangzhou, China, (2005).

In order to see related information, you need to Login.