Synthesis and Crystal Structure of Hexagonal DyMnO3

Abstract:

Article Preview

The magnetic properties were investigated on Co66Fe4B15Si15 amorphous ribbons of annealed at temperature range from 473 K to 773 K in vacuum (A-batch) and open air (B-batch). Static permeability from domain wall motion decreases with annealing temperature both in A- and B-batch sample. The permeability from magnetization rotation increases up to 700 K annealing temperature, but then decreases. The GMI profiles show a symmetric curve in A-batch samples irrespective of annealing temperature. In B-batch samples, symmetric profiles are shown up to 650 K annealing temperature, while they becomes asymmetric for further annealing temperature, due to the exchange bias-field induced by surface crystalline layer.

Info:

Periodical:

Materials Science Forum (Volumes 449-452)

Edited by:

S.-G. Kang and T. Kobayashi

Pages:

1045-1048

Citation:

N. Kamegashira et al., "Synthesis and Crystal Structure of Hexagonal DyMnO3", Materials Science Forum, Vols. 449-452, pp. 1045-1048, 2004

Online since:

March 2004

Export:

Price:

$38.00

[1] H. L. Yakel, W. C. Koehler, E. F. Bertaut and F. Forrat: Acta Cryst. vol. 16 (1963), p.957.

[2] W.C. Koehler, H. L. Yakel, E. O. Wollan and J. W. Cable: Phys. Lett., vol. 9 (1964), p.93.

[3] C. P. Khattak and F. F. Y. Wang: in Handbook on the Physics and Chemistry of Rare Earths, ed. by K. A. Gschneidner, Jr. and L. Eyring, Chap. 29, p.525, North-Holland Publ. Comp. (1979).

[4] A. Waintal and J. Chenavas: C. R. Acad. Sci. Paris, vol. 264 (1967), p.168.

[5] A. Waintal and J. Chenava: Mat. Res. Bull. vol. 2 (1967), p.819.

[6] H. W. Brinks, H. Fjellvag, and A. Kjekshus: J. Solid State Chem. vol. 129 (1997), p.334.

[7] E. F. Bertaut, F. Forrat and P. Fang: C. R. Acad. Sci. Paris. vol. 256 (1963), p. (1958).

[8] M. Isobe, N. Kimizuka, M. Nakamura and T. Mohri: Acta Cryst. vol. C47, (1991), p.423.

[9] H. W. Xu, J. Iwasaki, T. Shimizu, H. Satoh and N. Kamegashira: J Alloys Compds. vol. 221 (1995), p.274.

[10] G. Szabo and R. A. Paris: C. R. Acad. Sci. Paris, vol. 268 (1969), p.513.

[11] G. Chen, H. Takenoshita and N. Kamegashira: J. Alloys Compds. vol. 238 (1996), p.28.

[12] F. Izumi: J. Crystallogr. Jpn., vol. 27 (1985), p.23.

[13] F. Izumi: J. Mineralogical Soc. Jpn., vol. 17 (1985), p.37.

[14] T. Horikubi and N. Kamegashira: J. Alloys Compds. vol. 287 (1999), p.62.

[15] N. Kamegashira and Y. Hiyoshi: Mat. Lett. vol. 2 (1984), p.337.

[16] T. Atsumi, T. Ohgushi and N. Kamegashira: J. Alloys Compds. vol. 238 (1996), p.35.

Fetching data from Crossref.
This may take some time to load.