Influence of Annealing Temperature on Magnetic Properties in Co-Based Amorphous Ribbons

Abstract:

Article Preview

The magnetic properties were investigated on Co66Fe4B15Si15 amorphous ribbons of annealed at temperature range from 473 K to 773 K in vacuum (A-batch) and open air (B-batch). Static permeability from domain wall motion decreases with annealing temperature both in A- and B-batch sample. The permeability from magnetization rotation increases up to 700 K annealing temperature, but then decreases. The GMI profiles show a symmetric curve in A-batch samples irrespective of annealing temperature. In B-batch samples, symmetric profiles are shown up to 650 K annealing temperature, while they becomes asymmetric for further annealing temperature, due to the exchange bias-field induced by surface crystalline layer.

Info:

Periodical:

Materials Science Forum (Volumes 449-452)

Edited by:

S.-G. Kang and T. Kobayashi

Pages:

1049-1052

Citation:

L. Jin et al., "Influence of Annealing Temperature on Magnetic Properties in Co-Based Amorphous Ribbons", Materials Science Forum, Vols. 449-452, pp. 1049-1052, 2004

Online since:

March 2004

Export:

Price:

$38.00

[1] K. Mohri, T. Kohzawa, K. Kawashima, H. Yosida, L.V. Paina, IEEE Trans. Magn. Vol. 28 (1992), p.3150.

[2] L. Panina, K. Mohri, Appl. Phys. Lett. Vol. 65 (1994), p.1189.

[3] K. Mondal, S.K. Ghatak, Phys. Rev. B Vol. 47 (1993), p.14233.

[4] R.S. Beach, A.E. Berkowiz, Appl. Phys. Lett. Vol. 64 (1994), p.3652.

[5] J. Velazquez, M. Vazquez, D.X. Chen, S. Hernando, Phys. Rev. B Vol. 50 (1994), p.16737.

[6] F.L.A. Machado, C.S. Martins, Phys. Rev. B Vol. 65 (1994), p.1189.

[7] L.V. Panina, K. Mori, K. Bushida, M. Noda, J. Appl. Phys., Vol. 76 (1996), p.6198.

[8] T. Kitoh, K. Mohri, T. Ushiyama, IEEE Trans. Magn., Vol. 31 (1995), p.3137.

[9] C. G Kim, C.O. Kim, S.S. Yoon J. Magn. Magn. Mater., Vol. 249 (2002), p.293.

[10] S.S. Yoon, C.G. Kim, Appl. Phys. Lett., Vol. 78 (2001), p.3280.