Damage Behavior of Electron/Helium Dual-Beam Irradiation on Fe-Cr-Mn (W, V) Alloy


Article Preview

The effect of helium on irradiation damage behavior in Fe-Cr-Mn(W,V) steel was investigated by electron/helium ion dual-beam irradiation. The results indicate that helium can promote the increase of dislocation density and enhance the void nucleation and void swelling of Fe-Cr-Mn(W、V) alloy. The segregation of solute elements near grain boundary was suppressed by existence of helium. Also the interface of carbide-matrix migration and the change of solute concentration near the interface were observed during dual-beam irradiation.



Materials Science Forum (Volumes 475-479)

Main Theme:

Edited by:

Z.Y. Zhong, H. Saka, T.H. Kim, E.A. Holm, Y.F. Han and X.S. Xie




B. Hu et al., "Damage Behavior of Electron/Helium Dual-Beam Irradiation on Fe-Cr-Mn (W, V) Alloy", Materials Science Forum, Vols. 475-479, pp. 1463-1466, 2005

Online since:

January 2005




[1] H. Takahashi, Y. Shindo and H. Kinoshita: J. Nucl. Mater. Vol. 258-263(1988), pp.1644-1650.

[2] Hu Benfu and H. Takahashi: Chinese J. Nucl. Sci. and Eng. Vol. 17(1997), pp.143-149.

[3] W.G. Wolfer: Phil. Mag. Vol. 58A(1988), pp.285-297.

[4] W.G. Wolfer: Phil. Mag. Vol. 59A(1989), pp.183-103.

[5] N. Sakaguchi, S. Watanabe and H. Takahashi: Annales de physique. Vol. 22(1997), pp.142-147 10dpa/673K 0. 291nm M23C 0. 291nm M23C.