Effects of Deformation on Electric Conductivity in Al-Zr Alloys


Article Preview

Electric conducting behavior, sectional residual stress and texture in deformed Al-Zr alloy were investigated in order to investigate effect of deformation on electric conductance. {111} textures were developed in the wire of deformed Al-Zr alloy and most strong intensity of {111} texture was observed at the core in the cross section of the wire. Residual stress was mainly measured at the surface and , especially, measured at the core in the case of 4.5Φ wire, also, electric conductance was higher at the surface than at the core. This means that electric conductance might be affected by distribution of the residual stress.



Materials Science Forum (Volumes 475-479)

Main Theme:

Edited by:

Z.Y. Zhong, H. Saka, T.H. Kim, E.A. Holm, Y.F. Han and X.S. Xie




S. D. Park et al., "Effects of Deformation on Electric Conductivity in Al-Zr Alloys", Materials Science Forum, Vols. 475-479, pp. 1743-1746, 2005

Online since:

January 2005




[1] E. Nes: Acta Met. Vol. 20 (1972), p.449.

[2] S. D. Park, B. G. Kim and H.W. Lee: J. Kor. Inst. Met & Mater. Vol. 39 (2001), p.381.

[3] R. A. Strayer, W. Mackie, L. W. Swanson: Surf. Sci. Vol. 34 (1973), p.225.

[4] H. Ishii, K. Sugiyama, E. Ito and K. Seki: Adv. Mater. Vol. 11 (1999), p.605.

[5] S. H. Rhee, Thesis for doctor degree, The Univ. of Texas at Austin . (2001).

[6] I. Kim: Metal and Materials Vol. 2 (1996), p.169 Wires Measured property Core Middle Surface Residual stress, σ [MPa]. -13. 6±1. 6 0 -23. 6±0. 3 4. 5Φ wire Electric resistance, R[Ω], at 25℃ 0. 270[Ω] - 0. 273[Ω] Residual stress, σ.

Fetching data from Crossref.
This may take some time to load.