Texture Changes of Carbon Steel and Stainless Steel as a Result of Wear


Article Preview

In this research, surface texture changes of carbon steel AISI 1045 and stainless steel AISI 304 under simultaneous wear and corrosion were investigated. A solution of 3.5 % wt. NaCl was used as the corrosion agent and a pin-on-disk tribometer was employed to perform wear and corrosion wear tests.Texture investigations of the worn samples have shown texture changes after wear and corrosion-wear tests. In worn carbon steel samples after dry wear test, {011}<100> and {111} fiber texture components were developed in initially random oriented samples, whereas under corrosive-wear conditions, {111}<011> texture and {001}<110> texture were developed. In the stainless steel samples, {112}<110> texture component was observed under both dry and corrosive wear conditions, in the samples that had random grain orientations before corrosion and corrosion-wear tests.



Materials Science Forum (Volumes 495-497)

Edited by:

Paul Van Houtte and Leo Kestens






M. Reza Bateni et al., "Texture Changes of Carbon Steel and Stainless Steel as a Result of Wear", Materials Science Forum, Vols. 495-497, pp. 441-446, 2005

Online since:

September 2005




[1] H. Krause and A.H. Demirci: Wear Vol. 61 (1980), pp.325-332.

[2] P. Heilmann, W.A.T. Clark, and D.A. Rigney: Acta Metall. Vol. 31 (1983), pp.1293-1305.

[3] A. Ravikiran: Tribology Transactions Vol. 43 (2000), pp.287-292.

[4] M. Godec, M. Jenko: Materials and Manufacturing Technology Vol. 34 (2000), pp.359-364.

[5] Hans-J. Bunge: Steel Research Vol. 62 (1991), pp.530-541.

[6] Zoheir N. Farhat: Wear Vol. 250 (2001), pp.401-408.

[7] D.R. Wheeler and D.H. Buckley: Wear Vol. 33 (1975), pp.65-74.

[8] P.J. Alison and H. Wilman: British journal Applied Physics Vol. 15 (1964), pp.281-289.

[9] H. Krause and E. Ocalan: Wear Vol. 108 (1986), pp.337-343.

[10] G. Liu and B.J. Duggan: Metallurgical and Materials Transactions Vol. 32A (2001), pp.125-134.

[11] S. Mishra, C. Därmann and K. Lücke: Acta metall. Vol. 32 (1984), p. 2l85-2201.

[12] V.I. Yushkov, R. A. Adamescu, Y. S. Machnev, T. M. Gapeka and P. V. Geld: Materials Science and Engineering Vol. 64 (1984), pp.157-169.

DOI: 10.1016/0025-5416(84)90100-9

[13] B. Ravi Kumar, A.K. Singh, Samar Das, D.K. Bhattacharya, Materials Science and Engineering A Vol. 364 (2004), pp.132-139.

In order to see related information, you need to Login.