Sinterability of High-Speed Steels M2, M3/2 and T15
Hardmetal is usually processed by the conventional powder technology techniques: mix of WC + Co powders compacted and liquid phase sintering. A new method to process hardmetal parts is hereby described. Parts of WC-15%wt Co were processed by using high pressure – high temperature sintering. It was used the pressure of 5GPa, temperatures of 780-1200-1350-1400oC, and times of 2-4 minutes of sintering. Results are shown as a function of micro-structural evolution, densification, and hardness measurements.
Lucio Salgado and Francisco Ambrozio Filho
R. M. U. Nogueira and C. E. da Costa, "Sinterability of High-Speed Steels M2, M3/2 and T15", Materials Science Forum, Vols. 498-499, pp. 238-243, 2005