Fine-Grained Tungsten Heavy Alloy by Mechanical Alloying with Yttrium Oxide Addition

Abstract:

Article Preview

In this paper, the microstructure and mechanical properties of yttrium oxide dispersed 90W-7Ni-3Fe alloy were studied. The 90W-7Ni-3Fe nano-crystalline composite powder dispersed with Y2O3 addition was firstly fabricated by MA process, and then the powder was pressed and sintered at 1480°C for 30 min. A fine-grained 90W-7Ni-3Fe alloy with high tensile strength and elongation properties was obtained, in which the tungsten grain size was 8-12μm, the maximum tensile strength was 1050 MPa and the elongation was 30%. The Influence of rare earth oxide Y2O3 on the mechanical properties and microstructure characteristics is discussed in detail herein.

Info:

Periodical:

Materials Science Forum (Volumes 534-536)

Edited by:

Duk Yong Yoon, Suk-Joong L. Kang, Kwang Yong Eun and Yong-Seog Kim

Pages:

1261-1264

DOI:

10.4028/www.scientific.net/MSF.534-536.1261

Citation:

J. L. Fan et al., "Fine-Grained Tungsten Heavy Alloy by Mechanical Alloying with Yttrium Oxide Addition", Materials Science Forum, Vols. 534-536, pp. 1261-1264, 2007

Online since:

January 2007

Export:

Price:

$38.00

[1] S Yadav, K T Ramesh, in: Proceedings of the 1994 International Conference on Tungsten and Refractory Metals, MPIF, Princeton NJ, 1995, p.411~417.

[2] L S Magness, D Scheffler, T Weerasooriya, in: Tungsten, Hard Metals, and Refractory Alloys5-2000, MPIF NJ, 2000, p.35~44.

[3] D K Kim, S Lee, H J Ryu, et al: Metall & Mater Trans A Vol. 31(2000), p.2475~2489.

[4] J L Fan, B Y Huang, X H Qu: Trans of NF. Soc Vol. 1(2000), p.57~59.

[5] J Fan, B Huang, X Qu and K A Khalil: Int. J Powder Metall Vol. 38(2002), p.56~61.

[6] H J Ryu, S H Hong and W H Baek: Materials Science and Engineering A Vol. 291(2000), p.91~96.

[7] J L Fan, B Y Huang: Journal of Advanced Materials Vol. 36(2004), p.48~52.

[8] H J Ryu, S H Hong and W H Baek: Journal of Materials Processing Technology Vol. 63(1997), p.292~297.

In order to see related information, you need to Login.