Effect of different aging temperatures on microstructure and stress rupture properties of DZ951 alloy were investigated in this paper. The results show that the shape of carbide changed from script-like in as-cast alloy to block during different aging treatments. MC carbide degrades into M23C6 at the aging temperature of 970°C, which made alloy have a better combination of strength and ductility than that at other aging temperatures. The size of γ′ phase increases and the shape of γ′ phase changed from sphere (870°C) to quasi-cuboid (920°C) and cuboid (970°C) with the increasing aging temperature. The stress rupture life of DZ951 alloy at 1100°C/60MPa improves with the increased of aging temperature. The fractographs at different conditions showed a ductile fracture mode.