NiCr-CrAl Coating for Ni3Al Base Alloy IC6AE


Article Preview

The effect of NiCr-CrAl coating on the microstructure, oxidation and corrosion resistance, as well as mechanical properties of Ni3Al base alloy IC6AE has been studied in the present investigation. NiCr-CrAl coating for alloy IC6AE was prepared by the powder pack cementation method. The oxidation resistance tests were carried out under the condition of 1050°C/100h, while the hot corrosion resistance tests were under 900°C/100h. The tensile tests at the room temperature and the stress rupture life tests under 1050°C/90Mpa have been also conducted. The experimental results showed that NiCr-CrAl as-coated specimens had excellent oxidation and hot corrosion resistance compared with the alloy IC6AE blank specimens, and NiCr-CrAl coating has no obvious effect on the mechanical properties of alloy IC6AE. It may be concluded that NiCr-CrAl coating is suitable for the alloy IC6AE.



Materials Science Forum (Volumes 546-549)

Edited by:

Yafang Han et al.




S. S. Li et al., "NiCr-CrAl Coating for Ni3Al Base Alloy IC6AE", Materials Science Forum, Vols. 546-549, pp. 1467-1470, 2007

Online since:

May 2007




[1] Y. F. Han, Z.P. Xing etc., Material Science and Engineering , A239-240 (1997) 871-876.

[2] Y. F. Han, S.H. Li, Y. Jin, M.C. Chaturvedi, Material Science and Engineering , A192/193 (1995) 899-907.

[3] Xiao Cheng-bo, Han Ya-fang, Journal Of Rare Earths, 2000, vol. 18, No. 2.

[4] C.X. Zhang, , Beihang University, March, (2006).

Fetching data from Crossref.
This may take some time to load.