Effect of Low-Temperature Recovery Treatments on Subsequent Recrystallization in Al-2.5%Mg


Article Preview

The effect of low temperature recovery treatments on the recrystallization kinetics during subsequent high temperature annealing was investigated in three Al-2.5%Mg alloys with various Fe additions. Recovery treatments were carried out at 190oC for times ranging from 0.25 to 65 hrs. Recrystallization treatments were carried out at 280oC. The kinetics of recrystallization was followed using the techniques of hardness measurement, optical metallography and calorimetry.



Edited by:

P. B. Prangnell and P. S. Bate




B. Decreus et al., "Effect of Low-Temperature Recovery Treatments on Subsequent Recrystallization in Al-2.5%Mg", Materials Science Forum, Vol. 550, pp. 381-386, 2007

Online since:

July 2007




[1] T. Furu, K. Marthinsen and E. Nes: Materials Science and Technology. Vol 6 (1990), p.1094.

[2] H. P. Stuwe, A. F. Padilha and F. Siciliano Jr.: Materials Science and Engineering A. Vol 333 (2002), p.361.

[3] E. C. W. Perryman: Transactions AIME- Journal of Metals. Vol. 203 (1955), p.1053.

[4] N. Ryum and J. D. Embury: Scandinavian Journal of Metallurgy. Vol 11. (1982) p.51.

[5] R. Kaspar and J. Pluhar: Recrystallization of Previously Recovered Aluminium, Metal Science. Vol. 9 (1975), p.104.

DOI: 10.1179/030634575790444333

[6] F. J. Humphreys and M. Hatherly: Recrystallization and Related Annealing Phenomena, Pergomon Press, Oxford, (1996).

[7] J. K. Stanely: Transactions AIME. Vol 162 (1945). p.116.

[8] A. Rosen, M. S. Burton and G. V. Smith: Transactions of the Metallurgical Society of AIME. Vol 230 (1964), p.205.

[9] N. Ryum: Acta Metallurgica. Vol 17 (1969), p.831.

[10] C. J. Smithells, Smithells Metals Reference book, 8 th edition, Butterworths, London, (2004).

[11] M. Verdier, Ph.D. Thesis, INP Grenoble, (1997).

[11] M. Verdier, Y. Brechet and P. Guyot, Acta Materialia Vol. 47 (1999) p.127.

[12] M. F. Ashby, Philosophical Magazine Vol. 21, (1970) p.399.

Fetching data from Crossref.
This may take some time to load.