Tracing the Goss Orientation during Deformation and Annealing of an FeSi Single Crystal


Article Preview

A Goss-oriented single crystal was cold rolled up to 89 % thickness reduction, and subsequently annealed at 550°C or 850°C. During deformation most of the initially Goss-oriented material rotated into the two symmetrical {111}<112> orientations. In addition, Goss regions were observed related to microbands or microshear bands. Goss regions in microshear bands formed during straining, whereas Goss regions between microbands were retained from the initial Goss orientation. The recrystallisation texture for annealing temperatures of both 550°C and 850°C is characterised by a Goss texture. However, the origin of the Goss recrystallisation nuclei appeared to be different for the different annealing conditions. In the material annealed at 550°C, the Goss texture originated from the Goss regions in the microshear bands. In contrast, for an annealing temperature of 850°C, the Goss grains between the microbands are likely to form recrystallisation nuclei.



Edited by:

P. B. Prangnell and P. S. Bate




D. Dorner et al., "Tracing the Goss Orientation during Deformation and Annealing of an FeSi Single Crystal", Materials Science Forum, Vol. 550, pp. 485-490, 2007

Online since:

July 2007




[1] M. Matsuo: ISIJ Int. Vol. 29 (1989), p.809.

[2] A. Boettcher and K. Luecke: Acta Metall Mater. Vol. 41 (1993), p.2503.

[3] S. Mishra, C. Daermann and K. Luecke: Acta Metall. Vol. 32 (1984), p.2185.

[4] N. Pease, D. Jones, M. Wise and W. Hutchinson: Met Sci. Vol. 15 (1981), p.203.

[5] D. Dorner, S. Zaefferer and D. Raabe: Acta Mater, to be published.

[6] D. Dorner and S. Zaefferer, Texture and Anisotropy of Polycrystals II, Trans Tech Publications, C. Esling, M. Humpert, R. Schwarzer and F. Wagner (Eds. ), Switzerland, (2005), p.239.

[7] T. Haratani, W.B. Hutchinson, I.L. Dillamore and P. Bate: Metal Sci. Vol. 18 (1984), p.57.

[8] K. Tsusaki, H. Kobayashi, H. Tanaka and T. Maki: Recrystallisation, texture and their application to structural control, ISIJ (1999), p.40.

Fetching data from Crossref.
This may take some time to load.