SPF/DB Research in ZK60 Alloy with Gasification Agent as Pressurization Mediator

Abstract:

Article Preview

A new SPF/DB technology using gasification agent as pressurization mediator was proposed in this paper. The forming principle of SPF/DB using the agent was represented. Dies used for the forming process was designed and manufactured, and new gasification agent N11 which is white solid powder at normal temperature and it is easy to encapsulate and keep was developed for magnesium alloy. ZK60 magnesium alloy with a thickness of 1mm and grain size of 7.9μm was selected to conduct the experiment of SPF/DB. Corrugated ZK60 magnesium alloy parts were well formed under the temperature between 653K and 673K and forming time of 50 minutes. SEM was used to observe the microstructures of the diffusion bonding joints. The result shows that the joints were well bonded.

Info:

Periodical:

Materials Science Forum (Volumes 551-552)

Edited by:

K.F. Zhang

Pages:

241-244

Citation:

Y. D. Yu et al., "SPF/DB Research in ZK60 Alloy with Gasification Agent as Pressurization Mediator", Materials Science Forum, Vols. 551-552, pp. 241-244, 2007

Online since:

July 2007

Export:

Price:

$38.00

[1] J.C. Huang and T. H. Chuang: Materials Chemistry and Physics, Vol. 195-206 (1999).

[2] Y.W. Xun and M.J. Tan: Journal of Materials Processing Technology, Vol. 80-85 (2000).

[3] E.D. Weisert: Ti. Sci. and Techn, Vol. 1221-1228 (1984).

[4] B.L. Mordike and T. Ebert: Materials Science and Engineering A, Vol. 37-45 (2001). Fig. 2 Part for SPF/DB technology Fig. 3 Section pattern at bonding of wave component Fig. 4 Schematic representation of the internal balancing of dies caring.

Fetching data from Crossref.
This may take some time to load.