High Temperature Properties of CoFe/CoNi and Fe/CoNi Biphase Microwires


Article Preview

The objective of this work has been to analyze the high-temperature behavior of magnetically single-and biphase microwires because of its interest from fundamental and applications viewpoints. Two alloy compositions with amorphous structure covered by glass have been prepared as magnetically single phase microwires by quenching & drawing technique: CoFe-based with near zero saturation magnetostriction constant and Fe-based with positive saturation magnetostriction constant. The same wires were used as the core for magnetically biphase microwires. Second CoNi phase was deposited by electroplating. Magnitudes as saturation magnetization and hysteresis parameters are determined in the temperature range from room temperature up to 1200 K. We proceed to a comparative analysis of their magnetic behaviour at different temperatures as well as after cooling down to room temperature. Information on the Curie temperature of different phases and on the influence of heating process on the magnetic properties is thus derived.



Solid State Phenomena (Volumes 233-234)

Edited by:

Nikolai Perov and Anna Semisalova




I. Iglesias et al., "High Temperature Properties of CoFe/CoNi and Fe/CoNi Biphase Microwires", Solid State Phenomena, Vols. 233-234, pp. 265-268, 2015

Online since:

July 2015




* - Corresponding Author

[1] M. Vazquez, Advanced Magnetic Microwires, Handbook of Magnetism and Advanced Magnetic Materials, 2007, vol. 4, p.2193–2221.

DOI: https://doi.org/10.1002/9780470022184.hmm418

[2] A. Zhukov, V. Zhukova, Nova Science Publishers, 2009, vol. 11788, p.162.

[3] M. Vazquez, H. Chiriac, A. Zhukov, et al, Phys. Stat. Sol. A, 2010, pp.1-9.

[4] M. Ipatov, V. Zhukova, A.K. Zvezdin, et al, J. Appl. Phys., 2009, vol. 106, p.103902.

[5] K. Richter, R. Varga, et al, Appl. Phys. Lett., 2010, vol. 96, p.182507.

[6] V. Rodionova, M. Ipatov, M. Ilyn, V. Zhukova, et al, J. Appl. Phys., 2010, vol. 108, p.016103.

[7] H. Chiriac, S. Corodeanu, M. Lostun, G. Stoian, et al, J. Appl. Phys., 2011, vol. 109, p.063902.

[8] K. Pirota, M. Hernandez-Velez, et al, Adv. Funct. Mater., 2004, vol. 14, No. 3, p.266–268.

[9] M. Vazquez, K. Pirota, J. Torrejón, et al, J. Magn. Magn. Mat., 2006, vol. 304, pp.197-202.

[10] J. Torrejón, G. Badini, K. Pirota, M. Vázquez, Acta Materialia, 2007, vol. 55, p.4271.

[11] J. Escrig, S. Allende, D. Altbir, M. Bahiana, et al, J. Appl. Phys., 2009, vol. 105, p.023907.

[12] J. Torrejon, G. Badini-Confalonieri, et al, J. Appl. Phys., 2008, vol. 103, p. 07E712.

[13] G. Infante, G. A. Badini-Confalonieri, et al, J. Phys D: Appl. Phys., 2010, vol. 43, p.345002.

[14] H. Lumá, M. Vázquez, et al, J. Magn. Magn. Mat., 1999, vol. 196-197, pp.821-823.

[15] M. Vázquez, A. Zhukov, et al, Mater. Sci. and Engineer. A, 2004, vol. 375-377, pp.1145-1148.

[16] V. Rodionova, A. Nikoshin, et al, IEEE Trans Magn., 2011, vol. 47, № 10, pp.3787-3790.

[17] J. Torrejon, G. A. Badini-Confalonieri, et al, Sensor Letters, 2007, vol. 5, p.153 – 156.

Fetching data from Crossref.
This may take some time to load.